Increasing the electrode thickness, thereby reducing the proportion of inactive cell components, is one way to achieve higher-energy-density lithium-ion batteries. This, however, results in higher electronic and ionic overpotentials and/or mechanical failure induced by binder migration. Here, we report ethanol-induced phase inversion as an effective method for making high-mass-loading nickel-rich, layered oxide (LiNi0.8Mn0.1Co0.1O2 [NMC811]) electrodes. The ethanol-induced phase inversion electrodes significantly outperform their conventionally processed counterparts with similar loading (35 mg/cm2) and porosity (30%) in Li/NMC half-cells (131.7 mAh/g vs. 56.7 mAh/g) at 1C (7 mA/cm2) discharge. The binder structure induced by the nonsolvent improves the pore connectivity and results in lower tortuosity factors. The rapid solvent removal reduces the binder migration during drying, enabling ultrahigh active mass loadings up to 60 mg/cm2 (12 mAh/cm2). Further, the compatibility of the phase inversion process with current roll-to-roll coating setups makes this a processing technique with high industrial feasibility.@en

The growing demand for safe, cost-efficient, high-energy and high-power electrochemical energy storage devices has stimulated the development of aqueous-based supercapacitors with high capacitance, high rate capability, and high voltage. 2D titanium carbide MXene-based electrodes have shown excellent rate capability in various dilute aqueous electrolytes, yet their potential window is usually narrower than 1.2 V. In this study, we show that the potential window of Ti₃C₂T _x MXene can be efficiently widened to 1.5 V in a cost-effective and environmentally benign polyethylene glycol (PEG) containing molecular crowding electrolyte. Additionally, a pair of redox peaks at −0.25 V/−0.05 V vs. Ag (cathodic/anodic) emerged in cyclic voltammetry after the addition of PEG, yielding an additional 25% capacitance. Interestingly, we observed the co-insertion of the molecular crowding agent PEG-400 during the Li⁺ intercalation process based on in-situ x-ray diffraction analysis. As a result, Ti₃C₂T _x electrodes presented an interlayer space change of 4.7 Å during a complete charge/discharge cycle, which is the largest reversible interlayer space change reported so far for MXene-based electrodes. This work demonstrates the potential of adding molecular crowding agents to improve the performance of MXene electrodes in aqueous electrolytes and to enlarge the change of the interlayer spacing.

@en

Nanostructured solid composite electrolyte or nano-SCE, which is composed of an ionic liquid, nanoporous silica, and residuals of immobilized precursor components, shows promising synergistic properties. The ionic conductivity of nano-SCE is in the range of 2–5 mS cm⁻¹, which exceeds the bulk ionic liquid conductivity at ambient temperature, while maintaining characteristics of a solid electrolyte such as having no leakage issues as the ionic liquid is confined, and lower flammability compared to conventional liquid electrolytes. In this study, the underlying mechanism of enhanced conductivity is investigated by using magic angle spinning NMR and NMR relaxometry analysis. Water, one of the volatile precursor molecules has shown to play a key role in the final conductivity and stability at the solid-electrolyte interface, as it enhances the temperature range in which the ionic liquid remains mobile. In line with previous studies, water with lowered mobility is found in the silicon matrix. The activation energies of lithium ion transfer probed by NMR relaxometry, however, do not change as function of water content. The increase in bulk mobility of lithium ions under ambient conditions compared to water-less nano-SCE is found to be the origin of the altered conductivity of this material.

@en