Partial shading of PV modules can lead to degradation of the shaded cells. The degradation originates from a reverse bias voltage over the shaded cells. In order to mitigate reverse bias damage in Cu(In, Ga)Se2 (CIGS) modules, a good understanding of the fundamental mechanisms governing the reverse characteristic is required. In this study, a model is introduced that describes this behavior for CIGS cells. In this model, the low and non-Ohmic leakage current is accounted for by the space charge limited current component. A sharp increase in current that is typically observed in the CIGS reverse characteristics can be described by Fowler-Nordheim tunneling. This model has been validated against measurements performed at different temperatures and illumination intensities, and is able to describe the dependencies of the reverse bias behavior on both temperature and illumination.

When a PV module is partially shaded, the shaded solar cells operate in a reverse bias condition. For Cu(In,Ga)Se2 cells this condition can cause defects that irreversibly reduce the output of these cells and the full module. In order to design robust shade-tolerant CIGS modules details need to be known of the conditions at which these defects will be formed. In this study a large number of cells were exposed to different reverse bias conditions. By using simple statistics the probability of the occurrence of defects as a result of reverse bias at any given voltage has been determined. Based on our experiments we have found that the absorber thickness is one of the main parameters that affects the shade-tolerance: the thicker the absorber, the more shade tolerant the CIGS module will be.