Evaluation of the Aging Properties of Terminal Blend Hybrid Asphalt Based on Chemical and Rheological Methods

Abstract

The chemical and rheological properties of terminal blend hybrid asphalt (TBHA) contributing to the consumption of waste tires before and after aging were studied. Styrene-butadiene-styrene (SBS) polymer, sulphur, crumb rubber (CR), and neat asphalt were chosen to prepare the TBHA. The short-term aging (STA) and long-term aging (LTA) of TBHA were simulated using a rolling thin film oven test (RTFOT) and pressure aging vessel (PAV), separately. The chemical and rheological properties of the TBHA were tested. The results show that the G* and G*/sin δ of TBHA ares generally lower than SBS-modified asphalt (SBSMA) at 76 °C, and the δ, Jnr0.1, and Jnr3.2 of TBHA are generally higher than SBSMA at 76 °C. Additionally, with the decrease of CR, the G* and G*/sin δ of TBHA decreased more obviously, and the G* and G*/sin δ of 5T_3S_0.2Sul (5 wt% CR, 3 wt% SBS, and 0.2 wt% sulphur) were the smallest. Moreover, during the STA, the SBS modifier in the TBHA degraded and made the bitumen predominantly soft; however, during the LTA, the hardening of the bitumen played a dominant role and increased its elasticity. The superior anti-aging properties of TBHA (both STA and LTA) are further demonstrated.