On the effect of atomic layer deposited Al 2 O 3 on the environmental degradation of hybrid perovskite probed by positron annihilation spectroscopy

Journal article (2019)

Authors

Dibyashree Koushik Eindhoven University of Technology
J. Melskens Eindhoven University of Technology
Amber Nusteling Student
Valerio Zardetto Solliance Solar Research
H. Schut RST/Neutron and Positron Methods in Materials - AS
W. M.M. Kessels Eindhoven University of Technology, Solliance Solar Research
S.W.H. Eijt RST/Fundamental Aspects of Materials and Energy - AS
Mariadriana Creatore Eindhoven University of Technology, Solliance Solar Research
Research Group
RST/Neutron and Positron Methods in Materials (AS) (TU Delft)
More Info
expand_more

Published Date

2019

Language

English

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Faculty

Applied Sciences

Department

RST/Radiation, Science and Technology

Research Group

RST/Neutron and Positron Methods in Materials

Abstract


The degradation of hybrid perovskite films when exposed to ambient air is a major challenge for the development of perovskite-based photovoltaics at large scale. At present, little is known about the environmental degradation of perovskite films associated with the development of structural defects or open volumes (such as atomic vacancies, voids, crystallographic defects and grain boundary defects) in the lattice, and about the depth dependence of the structural degradation. Therefore, in this work, we use Doppler broadening-positron annihilation spectroscopy (DB-PAS) depth-profiling to gain insight into the structural degradation of CH
3
NH
3
PbI
3-x
Cl
x
perovskite when exposed to ambient air. In parallel, we investigate the effect of ultrathin (<1 nm) atomic layer deposited (ALD) Al
2
O
3
processed directly on top of the perovskite as a means to suppress the degradation process. Specifically, we infer that the perovskite degradation involves changes in open volumes in its crystal lattice. This could be caused by the ingress of H
2
O molecules into the cation vacancies. In parallel, chemical changes in the perovskite films upon decomposition are observed, accompanied by a decrease in the film thickness as a function of air exposure time. When the perovskite films are decorated with ALD Al
2
O
3
, the latter delays the thickness reduction of the perovskite layer during air exposure and also suppresses the changes in its open volumes and chemical transformations. Our findings illustrate that an improved understanding of the perovskite degradation process can be obtained using DB-PAS, especially when combined with other thin film characterization techniques, such as X-ray diffraction and X-ray photoelectron spectroscopy.