The leading edges of wind turbine blades are adhesively bonded composite sections that are susceptible to impact loads during offshore installation. The impact loads can cause localized damages at the leading edges that necessitate damage tolerance assessment. However, owing to the complex material combinations together with varying bondline thicknesses along the leading edges, damage tolerance investigation of blades at full scale is challenging and costly. In the current paper, we design a coupon scale test procedure for investigating bondline thickness effects on damage tolerance of joints after being subjected to localized impact damages. Joints with bondline thicknesses (0.6 mm, 1.6 mm, and 2.6 mm) are subjected to varying level of impact energies (5 J, 10 J, and 15 J), and the dominant failure modes are identified together with analysis of impact kinematics. The damaged joints are further tested under tensile lap shear and their failure loads are compared to the intact values. The results show that for a given impact energy, the largest damage area was obtained for the thickest joint. In addition, the joints with the thinnest bondline thicknesses displayed the highest failure loads post impact, and therefore the greatest damage tolerance. For some of the thin joints, mechanical interlocking effects at the bondline interface increased the failure load of the joints by 20%. All in all, the coupon scale tests indicate no significant reduction in failure loads due to impact, hence contributing to the question of acceptable localized damage, i.e., damage tolerance with respect to static strength of the whole blade.

Single-blade installation is a conventional method for installing blades on monopile-type offshore wind turbines. A jack-up crane vessel is commonly used, and individual blades are lifted to the tower top height and mated with the hub. The relative motions between the hub and blade root during the mating phase, partly due to wind-induced blade motion and partly due to wave-induced monopile motion, can induce substantial impact forces at the blade root. This can cause severe damage at the blade root connections and have a high potential to jeopardise the installation task. Mitigation measures are therefore required to limit the relative motion between the hub and the root during the mating process. In this article, we investigate the effects of a passive tuned mass damper (TMD) on the (1) impact velocities manifested between the blade root and hub during the mating phase and (2) its effect on the response-based limiting sea states. Time-domain multi-body simulations of an installation system characterising the mating operation with and without a TMD for collinear and misaligned wind and wave conditions have been performed, and the effectiveness of TMD for controlling the impact velocity is quantified. Furthermore, finite element analyses are performed to determine the threshold velocity of impact for a scenario in which a blade root with a guide pin suffers a sideways impact with the hub. It is found that the tuned mass damper can reduce the relative impact velocities by more than 40% and can substantially expand the allowable sea states and operability for the mating operation. Moreover, the effectiveness of TMD at reducing the impact velocity increases with increasing significant wave height (H_s); however, it decreases with increasing wind-wave misalignment and with shifts in the wave spectral peak period (T_p) away from the tuned frequency. The findings of the study can be utilised for planning safe and cost-efficient installation of latest-generation wind turbine blades.

Most wind turbine blades are assembled piece-by-piece onto the hub of a monopile-type offshore wind turbine using jack-up crane vessels. Despite the stable foundation of the lifting cranes, the mating process exhibits substantial relative responses amidst blade root and hub. These relative motions are combined effects of wave-induced monopile motions and wind-induced blade root motions, which can cause impact loads at the blade root’s guide pin in the course of alignment procedure. Environmental parameters including the wind-wave misalignments play an important role for the safety of the installation tasks and govern the impact scenarios. The present study investigates the effects of wind-wave misalignments on the blade root mating process on a monopile-type offshore wind turbine. The dynamic responses including the impact velocities between root and hub in selected wind-wave misalignment conditions are investigated using multibody simulations. Furthermore, based on a finite element study, different impact-induced failure modes at the blade root for sideways and head-on impact scenarios, developed due to wind-wave misalignment conditions, are investigated. Finally, based on extreme value analyses of critical responses, safe domain for the mating task under different wind-wave misalignments is compared. The results show that although misaligned wind-wave conditions develop substantial relative motions between root and hub, aligned wind-wave conditions induce largest impact velocities and develop critical failure modes at a relatively low threshold velocity of impact.