A structure-based modelling framework was established to simulate the three-dimensional autogenous shrinkage of cement paste. A cement hydration model, HYMOSTRUC3D-E, was used to obtain the microstructures and ionic concentrations of the cement paste. A lattice fracture model bas ...
This study is undertaken to explore the relationship between the reaction products and the drying shrinkage of alkali-activated slag (AAS) with the varying hydroxide dosage. AAS pastes were firstly produced with either Al(OH)3 or Mg(OH)2 to investigate the effects of hydroxide on ...
Non-uniform stresses, strains and microcracking of the concretes with three coarse aggregate sizes (5–10 mm, 10–16 mm, 16–20 mm) dried under 40% relative humidity (RH) for 60 days were quantified using digital image correlation and lattice fracture modelling. The influencing mech ...
New self-healing agents that can chemically bind seawater ions invading cracked cementitious materials were proposed. The potential of self-healing and binding of seawater ions were investigated by thermodynamic modeling. It was found that CaO-NaAlO2 and CaO-metakaolin ...
Concrete generally deforms and cracks in a non-uniform manner under drying-induced stress. This study used the lattice fracture model to simulate the drying-induced non-uniform deformations, stresses, and micro-crack propagation in concrete. Experiments were designed to validate ...

Effect of relative humidity on drying-induced damage in concrete

A comparative study of digital image correlation and lattice modelling

To assess the effect of relative humidity (RH) on drying-induced damage in concrete, the non-uniform strains and microcracks in concrete under different RH conditions were obtained using the digital image correlation (DIC) technique and lattice fracture model. The simulated non-u ...