3D hybrid perovskites (APbX₃) have made a significant impact on the field of optoelectronic materials due to their excellent performance combined with facile solution deposition and up-scalable device fabrication. Nonetheless, these materials suffer from environmental instability. To increase material stability, the organic cation (A) is substituted by the non-volatile cesium cation. However, the desired photoactive cesium lead(II) iodide black phase is metastable in ambient conditions and spontaneously converts into the photo-inactive yellow δ-phase. In this work, the black phase is stabilized by the formation of a quasi-2D perovskite containing a benzothieno[3,2-b]benzothiophene (BTBT) large organic ammonium cation. Thermal analysis shows that degradation of the butylammonium (BA)-based quasi-2D perovskite (BA)₂CsPb₂I₇ sets in at ≈130 °C, while (BTBT)₂CsPb₂I₇ is phase-stable until ≈230 °C. Additionally, the (BTBT)₂CsPb₂I₇ film does not show any sign of degradation after exposure to 77% Relative Humidity in the dark for 152 days, while (BA)₂CsPb₂I₇ degrades in a single day. Photoconductor-type detectors based on (BTBT)₂CsPb₂I₇ demonstrate an increased external quantum efficiency and a similar specific detectivity compared to the BA-based reference detectors. The results demonstrate the utility of employing a BTBT cation within the organic layer of quasi-2D perovskites to significantly enhance the stability while maintaining the optoelectronic performance.

2D layered hybrid perovskites are currently in the spotlight for applications such as solar cells, light-emitting diodes, transistors and photodetectors. The structural freedom of 2D layered perovskites allows for the incorporation of organic cations that can potentially possess properties contributing to the performance of the hybrid as a whole. In this study, we incorporated a benzothieno[3,2-b]benzothiophene (BTBT) alkylammonium cation into the organic layer of a 2D layered lead iodide perovskite. The formation and degradation of this material are discussed in detail. It is shown that the use of a solvent vapour annealing method significantly enhances the absorption, emission and crystallinity of films of this 2D layered perovskite as compared to regular thermal annealing. The photoconductivity of the films was determined using time-resolved microwave conductivity (TRMC) as well as in a device. In both cases, the solvent vapour annealed films show markedly higher photoconductivity than the films obtained using the regular thermal annealing approach.