A combined experimental and modelling study into the Pb-Mo-O system has been conducted in view of the safety analysis for lead-cooled nuclear systems. The thermal expansion and low-temperature heat capacity of the ternary compounds PbMoO4 and Pb2MoO5 have been determined experimentally, as well as the melting enthalpy of PbMoO4. Moreover, XANES measurements have confirmed the hexavalent oxidation state of Mo in PbMoO4 and Pb2MoO5.

A thermodynamic model of the ternary system including the ternary phases PbMoO4, Pb2MoO5 and Pb5MoO8 has also been developed in this work based on the CALPHAD methodology. For the first time, an ionic two-sublattice model is used for the liquid phase, while the compound energy formalism is used for the solid phases.@en

The thermochemistry of the ternary system CsI-PbI₂-BiI₃, of interest for applications in photovoltaics, memory devices, and nuclear applications, among other things, is investigated in this work. The binary phase diagrams CsI-PbI₂ and CsI-BiI₃ were subjected to renewed experimental investigation, and the compounds CsPbI₃, Cs₄PbI₆, and Cs₃Bi₂I₉ were found to be the only stable phases in the investigated temperature window. The liquidus lines and invariant equilibria were determined. The phase equilibria in the BiI₃-PbI₂ system were measured for the first time by using Differential Scanning Calorimetry (DSC). The end-members form a solid solution over the entire composition range. The pseudobinary section CsPbI₃-Cs₃Bi₂I₉ of the CsI-PbI₂-BiI₃ ternary system was moreover measured by DSC, as well as the ternary eutectic points. A thermodynamic model of the complete CsI-PbI₂-BiI₃ system was developed by using the Compound Energy Formalism (CEF) for the solid phases and the Modified Quasichemical Model in the Quadruplet Approximation (MQMQA) for the liquid phase. The binary systems were modeled first, and no ternary interaction parameters were found necessary to reproduce accurately the phase equilibria in the ternary system. With our model, the whole liquidus surface of the field CsI-PbI₂-BiI₃ is described for the first time.

@en

The quaternary compound Cs₂Pb(MoO₄)₂ was synthesized and its structure was characterized using X-ray and neutron diffraction from 298 to 773 K, while thermal expansion was studied from 298 to 723 K. The crystal structure of the high-temperature phase β-Cs₂Pb(MoO₄)₂ was elucidated, and it was found to crystallize in the space group R3̅m (No. 166), i.e., with a palmierite structure. In addition, the oxidation state of Mo in the low-temperature phase α-Cs₂Pb(MoO₄)₂ was studied using X-ray absorption near-edge structure spectroscopy. Phase diagram equilibrium measurements in the Cs₂MoO₄-PbMoO₄ system were performed, revisiting a previously reported phase diagram. The equilibrium phase diagram proposed here includes a different composition of the intermediate compound in this system. The obtained data can serve as relevant information for thermodynamic modeling in view of the safety assessment of next-generation lead-cooled fast reactors.

@en

The heat capacities of CsPbI₃, Cs₄PbI₆, and Cs₃Bi₂I₉ were studied using low-temperature thermal relaxation calorimetry in the temperature range of 1.9-300 K. The three compounds are insulators, with no electronic contribution to the heat capacity. None of them show detectable anomalies in the studied temperature window. Thermodynamic properties at standard conditions are derived. Previously reported results on Cs₃Bi₂I₉ are not fully consistent with the present findings. Moreover, the magnetic susceptibilities of the three title compounds were measured.

@en