We have investigated in detail properties of hybrid polyelectrolyte-anion exchange membranes (AEMs) having different amounts of a guanidinium-modified poly(allylamine hydrochloride) (PAH-Gu) derivative (2, 5, and 8 wt%). The presence of guanidinium groups at the membrane surface was confirmed by XPS. For 2 and 5 wt% the blended membranes are homogeneous, while at 8 wt% segregation is observed by AFM. The membrane permselectivity and ionic electrical resistance for phosphate reduce upon incorporation of the PAH-Gu in the membrane, reflecting an increased co-ion (H⁺ and Na⁺) permeation. We conclude that PAH-Gu loaded in the AEM favors an interaction with phosphate. In electrodialysis, using sodium sulfate and sodium dihydrogen phosphate at equal concentrations in the source phase a slight preference for phosphate was observed. Our work shows that this facile membrane fabrication procedure shows great potential in terms of tuning the membrane properties. One way to boost selective ion transport could be by increasing the number of functional groups in the membrane.

In this study, the preparation of a new, functional anion-exchange membrane (AEM), containing guanidinium groups as the anion-exchanging sites (Gu-100), is described as well as the membrane characterization by XPS, water uptake, permselectivities, and electrical resistances. The functional membrane was also employed in pH-dependent electrodialysis experiments using model dairy wastewater streams. The properties of the new membrane are compared to those of a commercially available anion-exchange membrane bearing conventional quaternary ammonium groups (Gu-0). Guanidinium was chosen for its specific binding properties toward oxyanions: e.g., phosphate. This functional moiety was covalently coupled to an acrylate monomer via a facile two-step synthesis to yield bulk-modified membranes upon polymerization. Significant differences were observed in the electrodialysis experiments for Gu-0 and Gu-100 at pH 7, showing an enhanced phosphate and citrate transport for Gu-100 in comparison to Gu-0. At pH 10 the difference is much more pronounced: for Gu-0 membranes almost no phosphate and citrate transport could be detected, while the Gu-100 membranes transported both ions significantly. We conclude that having guanidinium groups as anion-exchange sites improves the selectivity of AEMs. As the presented monomer synthesis strategy is modular, we consider the implementation of functional groups into a polymer-based membrane via the synthesis of tailor-made monomers as an important step toward selective ion transport, which is relevant for various fields, including water treatment processes and fuel cells.