A novel strategy of liquid fermentation using anaerobic dynamic membrane reactor (AnDMBR) was proposed to enhance volatile fatty acids (VFAs) production from sewage sludge. Results indicated that liquid sludge fermentation in AnDMBR had the potential in commercial VFAs production. VFAs productivity and concentration as well as substrate conversion rate could reach as high as 7.8 kg VFA−COD/m³ d, 60 g/L and 0.38 kg VFA−COD/kg VS, respectively. Moreover, dynamic membrane was stably operated for approximately 70 days. During the operational period, membrane flux was increased from 6.25 to 25 L/m² d and only once online membrane cleaning was implemented. Results of microbial analyses showed bacterial richness and evenness in AnDMBR were increased by membrane separation and organic loading rate (OLR) increase, but reduced by excessive OLR, which should led the variations in the performances of AnDMBR. Furthermore, the necessity of liquid sludge fermentation for VFAs production was further confirmed by economic assessment and the bioavailability analysis of the residual solids in pretreated sludge. The residual solid was proved to be not conducive to enhance VFAs yield. Conversely, the energy consumption for VFAs production could be reduced from over 100 to below 20 kwh/kg VFAs by avoiding the “useless” residual solids entering into fermenters.

@en

Frost action is the major threat against durability of concrete under cold region. Surface scaling and internal damage are the two main deterioration phenomenon caused by frost action. Nowadays, there is still a debate about whether surface scaling and internal damage caused by the same mechanism because of lacking direct experimental evidence. To prove that salt scaling is not analogous to internal damage, a rigid restraining ring is applied on concrete to simulate the real stress condition of concrete. Both relative dynamic modulus (RDM) and weight of surface scaling (SS) are recorded after every 4 cycles for both restraint specimens and free concrete. For the same mix proportion, the decrease of RDM of restraint specimens is less than that of free specimens, while the increase of SS of restraint specimens is higher than that of free specimens. The less decrease of RDM of restraint specimen is as expected due to the improvement of internal bond by rigid restraining ring. However the increment of SS of restraint specimens is more than that of free specimens prove that surface scaling and internal damage of concrete under frost action are dominant by different mechanisms directly. It is recommended that the testing of frost resistance shall be conducted on concrete with steel restraining ring.@en

At present several methods are available to predict the durability of reinforced concrete structures. In most cases, one dominant deterioration process such as carbonation or chloride penetration is taken into consideration. Experimental results as well as observations in practice show that this is not a realistic and certainly not a conservative approach. In order to test more realistically, RILEM TC 246-TDC, founded in 2011, has developed a method to determine the durability of concrete exposed to the combined action of chloride penetration and mechanical load. In this report, a test method is presented which allows determination of realistic diffusion coefficients for chloride ions in concrete under compressive or tensile stress. Comparative test results from five different laboratories showed that the combination of mechanical and environmental loads may be much more severe than a single environmental load without mechanical loading. Modelling and probabilistic analysis also showed that the obvious synergetic effects cannot be neglected in realistic service life prediction.

@en