Effect of P₂O₅ incorporated in slag on the hydration characteristics of cement-slag system

Abstract

This paper presents the influence of P₂O₅ incorporated in slag on the hydration characteristics of cement-slag system. It was found that the gradual addition of phosphorus oxide in slag did not change overall mineralogy of the hydration products. Except hydration retardation in the dormant stage, chemically bound water and portlandite contents, hydration degree of slag, and pore structure at all investigated ages were similar among cement-slag pastes with different P₂O₅ percentages. Furthermore, significantly higher amount of monosulfate was observed as the P₂O₅ content in slag increased. In addition, a higher Al/Si atomic ratio was measured in the C-S(A)-H gel phase formed in the cement matrix. However, similar Ca/Si atomic ratio of C-S(A)-H gel phase and Mg/Al atomic ratio of hydrotalcite-like phase were determined in all slag pastes, irrespective of the addition of P₂O_5. In contrast to magnesium ion which was retained within the original slag boundary, phosphorus ions could migrate into cement matrix. Therefore, P/Si atomic ratio of the C-S-H gel phase increased with the increasing phosphorus oxide content in slag, reaching up to ∼0.08.