Cleavage fracture micromechanisms in thick-section quenched and tempered S690 high-strength steels

Journal article (2022)

Authors

V. Morete Barbosa Bertolo Team Vera Popovich - Mechanical, Maritime and Materials Engineering
Quanxin Jiang Team Vera Popovich - Mechanical, Maritime and Materials Engineering
U. Tiringer Team Arjan Mol - Mechanical, Maritime and Materials Engineering , Team Peyman Taheri - Mechanical, Maritime and Materials Engineering
C.L. Walters Ship Hydromechanics and Structures - Mechanical, Maritime and Materials Engineering , TNO
J. Sietsma Team Kevin Rossi - Mechanical, Maritime and Materials Engineering
V. Popovich Team Vera Popovich - Mechanical, Maritime and Materials Engineering
Research Group
Team Vera Popovich (Mechanical, Maritime and Materials Engineering) (TU Delft)
Copyright: © 2022 V. Morete Barbosa Bertolo, Quanxin Jiang, U. Tiringer, C.L. Walters, J. Sietsma, V. Popovich
DOI: https://doi.org/10.1007/s10853-022-07841-1
More Info
expand_more

Published Date

2022

Language

English

Faculty

Mechanical, Maritime and Materials Engineering

Department

Materials Science and Engineering

Research Group

Team Vera Popovich

Abstract

For structural assessment and optimal design of thick-section high-strength steels in applications under harsh service conditions, it is essential to understand the cleavage fracture micromechanisms. In this study, we assess the effects of through-thickness microstructure of an 80-mm-thick quenched and tempered S690 high-strength steel, notch orientation, and crack tip constraint in cleavage nucleation and propagation via sub-sized crack tip opening displacement (CTOD) testing at −100 °C. The notch was placed parallel and perpendicular to the rolling direction, and the crack tip constraint was analysed by varying the a/W ratio: 0.5, 0.25, and 0.1. The notch orientation does not play a role, and the material is considered isotropic in-plane. Nb-rich inclusions were observed to act as the weak microstructural link in the steel, triggering fracture in specimens with the lowest CTOD values. While shallow-cracked specimens from the top section present larger critical CTOD values than deep-cracked ones due to stress relief ahead of the crack tip, the constraint does not have a significant influence in the middle due to the very detrimental microstructure in the presence of Nb-rich inclusions. Some specimens show areas of intergranular fracture due to the combined effect of C, Cr, Mn, Ni, and P segregation along with precipitation of Nb-rich inclusions clusters on the grain boundaries. Several crack deflections at high-angle grain boundaries were observed where the neighbouring sub-structure has different Bain axes.